| 性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
| 基本性能 |
吸水率 |
24hr in 23℃ |
ASTM D-570 |
0.17 |
% |
| 物理性能 |
比重 |
--- |
JIS K-7112 |
1.26 |
--- |
| 透光率 |
3mm thick |
ASTM D-1003 |
Translucent |
% |
| 阻燃性 |
1.5mm |
UL 94 |
V-2 |
--- |
| 機(jī)械性能 |
| 拉伸強(qiáng)度 |
屈服點(diǎn) |
| 斷裂點(diǎn) | |
--- |
|
|
| Mpa(kgf/cm2) |
| Mpa(kgf/cm2) | |
| 拉伸模量 |
--- |
ASTM D-638 |
2300(23500) |
Mpa(kgf/cm2) |
|
|
--- |
|
|
|
| 壓縮強(qiáng)度 |
--- |
ASTM D-695 |
73(740) |
Mpa(kgf/cm2) |
| 耐沖擊強(qiáng)度值 |
艾氏、帶缺口厚度3.2mm |
ASTM D-256 |
290(30) |
J/m(kgf・cm/cm) |
| 耐沖擊強(qiáng)度值 |
艾氏、帶缺口厚度6.4mm |
ASTM D-256 |
120(12) |
J/m(kgf・cm/cm) |
| 洛氏硬度 |
--- |
ASTM D-785 |
67 |
M標(biāo)度 |
| 電氣性能 |
絕緣破壞強(qiáng)度 |
快速加壓值厚度1.6mm |
ASTM D-149 |
30 |
kv/mm |
| 體積電阻率 |
--- |
ASTM D-257 |
3×1016 |
Ω.cm |
| 耐電弧性 |
--- |
ASTM D-495 |
100 |
sec |
| 耐導(dǎo)電徑跡性（CTI） |
--- |
IEC 112 |
340 |
V |
| 介電率 |
60Hz |
ASTM D-150 |
2.85 |
--- |
| 介電率 |
106Hz |
ASTM D-150 |
2.8 |
--- |
| 介電正切 |
60Hz |
ASTM D-150 |
0.0008 |
--- |
| 介電正切 |
106Hz |
ASTM D-150 |
0.008 |
--- |
| 加工性能 |
|
--- |
|
|
|
| 熱 性 能 |
| 線膨脹系數(shù) |
流動(dòng)方向 |
| 垂直方向 | |
--- |
|
|
|
| 負(fù)荷撓曲溫度 |
負(fù)荷0.451MPa(4.6kgf/cm2) |
JIS K-7207 |
145 |
℃ |
| 負(fù)荷撓曲溫度 |
負(fù)荷1.813MPa(18.6kgf/cm2) |
JIS K-7207 |
136 |
℃ |
| 溫度指數(shù) |
電學(xué)式 |
| 沖擊式 |
| 非沖擊式 | |
| 厚度1.47mm |
| 厚度1.47mm |
| 厚度1.47mm | |
|
|
|